Fiberglass Chopped Strand Mat

Attributes
Model Number: EMC450
Technique: Chopped Strand Fiberglass Mat (CSM)
Mat Type: Continuous Filament Mat
Fiberglass Type: E-Glass
Softness: Soft
Color: White
Width: 1040/1270mm
Weight: 450g/m2
Binder Type: Binder Type:
Moisture Content: ≤0.20%

Chopped strand mat is made of fiberglass chopped strands bonded with powder or emulsion binder uniformly.

Application:

It is compatible with polyester, vinyl and epoxy resin and widely used in boat building,autonotive, cooling towers, bathroom accessories, anti-corrosion pipes etc, suitable for hand lay up, filament winding, press molding forming processes.

Specification:

Code

Weight

(g/m2)

Binder   Type

L.O.I

(%)

Moisture   Content

(%)

T.   Strength (N)

Vertical

Horizontal

EMC100

100

Powder/Emulsion

4.0-12.0

≤0.2

≥80

≥80

EMC120

120

Powder/Emulsion

4.0-12.0

≤0.2

≥80

≥80

EMC150

150

Powder/Emulsion

4.0-12.0

≤0.2

≥100

≥100

EMC200

200

Powder/Emulsion

4.0-12.0

≤0.2

≥100

≥100

EMC225

225

Powder/Emulsion

2.0-8.0

≤0.2

≥100

≥100

EMC300

300

Powder/Emulsion

2.0-8.0

≤0.2

≥120

≥120

EMC380

380

Powder/Emulsion

2.0-8.0

≤0.2

≥120

≥120

EMC450

450

Powder/Emulsion

2.0-8.0

≤0.2

≥150

≥150

EMC600

600

Powder/Emulsion

2.0-8.0

≤0.2

≥150

≥150

*Specific products could be made according to customers’requirements.

Remarks:

Roll width: Standard width in 1040mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 3200mm.

Packing: Fiberglass chopped strand mat is usually rolled in a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.

Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.