Vacuum Bagging Films

Attributes
Material: PA-PE-PA
Film Thickness: 55-75Microns
Film Colour: Transparent Green

The Vacuum Bagging Film is widely used in Advance Composites Industries. This film is used to cover and seal the mould surface under vacuum condition in the process called Vacuum Infusion. This film is widely used due to is excellent physical properties such as high temperature resistance, toughness, good flexibility, high elongation and very less permeability.

Features:

l  Normally colour is green heat stabilized and material is nylon

l  It has excellent elongation and heat ageing characteristics capable of performing under high pressures and temperatures of up to 190°C for several hours

l  A Caprolactam level of less than 1% makes it an ideal choice for most vacuum bagging applications

l  It can be made available in different forms eg: lay flat or slit tube and in sheet form

Specification:

Parameters

Physical Parameters-55 Microns

Physical Parameters-65 Microns

Physical Parameters-75 Microns

Material

PA-PE-PA

PA-PE-PA

PA-PE-PA

Film   Thickness

55   Microns

65   Microns

75   Microns

Film   Colour

Transparent   Green

Transparent   Green

Transparent   Green

Resin   Compatability

Styrene   + Epoxy  

Styrene   + Epoxy  

Styrene   + Epoxy  

Standard   Width (Lay Flat)

600MM,   800MM,1200MM, 2000MM, 4000MM

600MM,   800MM,1200MM, 2000MM, 4000MM

600MM,   800MM,1200MM, 2000MM, 4000MM

Working   Temperature

Maximum   Upto 180°C

Maximum   Upto 180°C

Maximum   Upto 180°C

Storage & Handling

Packing

The   roll will be wrapped in polyethylene/bubble sheet over and above covered with   hard card board case for protecting it from piercing or damaging from the   pointed or hard material.

Handling

Roll   has to be handled properly having taken care roll doesn't get damanged or   pierced.

Storage

Has to   be stored in the place where the sharp edges are not there.Has to be stored   at room temperature and low moisture level place.

*NoteWide range of film can be undertaken for development based on the customer requirement where the application is at different temperature and for different purpose.