HITEX CORE PX is an engineered, cost-effective solution for closed mould composite processes, distinguished as a pressure-stable polyester non-woven fabric that uniquely functions as both a core material and an infusion medium. It is fully compatible with all conventional resin systems, including Unsaturated Polyester Resin, Vinyl ester, Phenolic, and Epoxy,and is thus perfectly suited for sophisticated closed mould techniques such as Infusion, RTM Light, and RTM Heavy.
Feature
The product has a diversion groove as a diversion medium; No need to use additional diversion materials
Better compressive performance
As a choice for low-cost core materials
Reduce product weight
Increase product rigidity
Can make the appearance of the product more beautiful
Excellent conformal performance
Excellent impact resistance
The thickness of the product can be controlled as needed
Max thickness 10mm, hexagonal core with non-absorbing resin, low compression rate (10%@-0.8bar)
Flow channel 0.5mm, between adjacent hexagons to accelerate resin flow
Application
Marine: hulls, decks and structures of boats and yachts
Transportation: parts and panels of cars, trailers, trucks and RV’s
Mass transit: interior and exterior of trains, light rail and buses
Leisure: kayaks, surfboards, pools and tubs ,Swimming Pool and bathroom
Industrial: Furniture , cladding panels, fans, containers and tanks
Wind energy:nacelle covers and spinners
BASIC PROPERTIES
HITEX Coremat grades match Lantor Coremat grades | |||
HITEX Coremat Grade | Equivalent Lantor Coremat Grade | Thickness | Width × Length (m) |
PS 2 | SF 2 | 2MM | 1.27*80 |
PS 3 | SF 3 | 3MM | 1.27*50 |
PM 1.5 | XF 1.5 | 1.5MM | 1.27*100 |
PM 2 | XF 2 | 2MM | 1.27*80 |
PM 3 | XF 3 | 3MM | 1.27*50 |
PM 4 | XF 4 | 4MM | 1.27*40 |
PM 5 | XF 5 | 5MM | 1.27*30 |
PM 6 | XF 6 | 6MM | 1.27*25 |
PT 1.5 | TF 1.5 | 1.5MM | 1.27*120 |
PT 2 | TF 2 | 2MM | 1.27*80 |
PT 3 | TF 3 | 3MM | 1.27*50 |
PX 1.5 | LRC 1.5 | 1.5MM | 1.27*70 |
PX 2 | LRC 2 | 2MM | 1.27*60 |
PX 3 | LRC 3 | 3MM | 1.27*40 |
Properties | PX 1.5 | PX 2.0 | PX 3.0 | |
Thickness | mm | 1.5 | 2.0 | 3.0 |
Thickness loss at 0,8bar | % | <10 | <10 | <10 |
Roll length | m | 70 | 60 | 40 |
Roll width | m | 1.27 | 1.27 | 1.27 |
Max processing temperature | °C | 180 | 180 | 180 |
Dry weight | g/m² | 120 | 150 | 220 |
Resin uptake | kg/m²/mm | 0.3-0.4 | ||
Density impregnated | kg/m³ | 400-500 | ||
*Specific products could be made according to customers’requirements.
TYPICAL MECHANICAL PROPERTIES（WITH UNSATURATED POLYESTER RESIN)
Mechanical properties | Unit | Value | Test Method |
Flexural strength | Mpa | 15 | ASTM D790 |
Flexural modules | Mpa | 1100 | ASTM D790 |
Tensile strength across layers | Mpa | 4 | ASTM C297 |
Compression strength:10%strain | Mpa | 5 | ISO 844 |
Shear strength | Mpa | 5 | ASTM C273-61 |
Shear modules | Mpa | 30 | ASTM C273-61 |
Notes:
The information contained in this document has been compiled in good faith by HITEX COMPOSITE (Ningbo) Co., Ltd., but nevertheless no representation or warranty is given as to the accuracy or completeness of the (technical) information provided herein. HITEX COMPOSITE (Ningbo) Co., Ltd., can not be held liable of any damages arising from any (printing) errors or omissions in this information. HITEX COMPOSITE (Ningbo) Co., Ltd., reserves the right to make changes with respect to the information provided at any without further notice.